Alloy Steel Products Description 14NiCr14/12CrNi3 steel belongs to alloy carburizing steel and has higher hardenability than 12CrNi2A steel. Therefore, it can be used to manufacture parts with slightly larger section than 12CrNi2A steel. The steel has good comprehensive mechanical properties after quenching, low temperature tempering or high temperature tempering. The steel has good low-temperature toughness, small notch sensitivity, and good cutting performance. When the hardness is HB260~320, the relative cutting processability is 60%~70. In addition, the steel has low hardness and good plasticity after annealing. Therefore, both cutting and cold extrusion methods can be used to manufacture the mold. In order to improve the wear resistance of the mold cavity, the mold needs to be carburized after molding, and then quenched and tempered at low temperature to ensure that the mold surface has high hardness, high wear resistance and the center has good toughness. This steel is suitable for manufacturing large and medium-sized plastic molds. 14NiCr14 Characteristics and Scope of Application 鈥?14NiCr14/1.5752 steel is a high-grade carburizing steel with a wide range of uses. Compared with 15Cr and 20Cr steels, it has high strength, plasticity and hardenability. 聽 14NiCr14 Steel Applications 14NiCr14/1.5752 steel mainly used to make the spindle with high strength, high hardness and high toughness under heavy load, and the shaft and rod with high center toughness or bearing impact load, surface abrasion resistance, small heat treatment deformation, as well as various transmission gears, adjusting screws and camshafts working under high speed and impact load. Products parameters Equivalent grades: GBISCCNSJISKSASTM/AISIUNSISODIN EN/DINW-Nr. 12CrNi3A42122SNC815SNC815 SNC815HSNC8153310G3310615NiCr1314NiCr141.5752 聽 Chemical composition (%) ComponentCSiMnPSCrNiCuMo Minimum value0.10.170.3--0.253.25-- Maximum value0.160.370.60.0350.0351.653.650.30.15 聽 Physical Property Elastic modulus E/GPaSpecific heat capacity 聽c/J路(g路K)-1Thermal conductivity位/W路(m路K)-1 20掳C380鈩?/div> 60鈩?/div> 100鈩?/div> 300鈩?/div> 500鈩?/div> 750鈩?/div> 2040.65730.98--25.5420.93 Coefficient of linear expansion伪/10-6 路K-1 20锝?00鈩?/div> 20锝?00鈩?/div> 20锝?00鈩?/div> 20锝?00鈩?/div> 11.81314.715.6 聽 Product Description 聽 Delivery conditioncold drawn, quenchen and tempered, centerless grinding Processing ServiceCold drawn,Grinding,Peeling,Heat treat ment Surface treatmentBlack, Grinded, Peeled, Rough turned, Polished Diameter2-90 mm (tolerance ISO h7,h8,h9) Applicationcold die,blanking die,punches and variour molding tools Delivery hardnessquenched & tempered 58-62HRC annealed condition 鈮?55HB PackingWater proof packing 聽 Product Picture Our factory Steel Making Ingot Production Forged Bars Machinary Mill鈥瞫 test certificate: Issued in English, in addition the normal terms, production process, the mechanical property (yield strength, tensile strength, elongation and hardness), forged ratio, UT test result, Grain size, heat treatment methods and the sample of is shown on the Certificate of Quality. EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing. Ultrasonic test:聽According to SEP 1921-84 C/c, D/d, E/e DIN1.5752/ 14NiCr14 Alloy Steel Heat treatment specification and metallographic structure:聽 Heat treatment specification: quenching: 860 鈩?for the first time, 780 鈩?for the second time, oil cooling; Temper at 200 鈩? water cooling and air cooling. Delivery status:Delivery in heat treatment (normalizing, annealing or high temperature tempering) or non heat treatment status. SURFACE FINISHES: Black, grinded, rough turned, turned by machine The application case 聽 Applications High strength, high hardness and high toughness under heavy load, and the shaft and rod with high center toughness or bearing impact load, surface abrasion resistance, small heat treatment deformation, as well as various transmission gears, adjusting screws and camshafts working under high speed and impact load. 聽聽 Our Service Payment terms: T/T 30% deposit and the 70% balance after finished production. Delivery condition: For abundant stock, 7-10 days. For customized products, 30-40 daysAlloy Steel website:http://www.htspecialmetals.com/alloy-steel/